 內(nèi)容編輯

POLYFLON™ M-18
聚四氟乙烯
DAIKIN AMERICA, INC.

產(chǎn)品說(shuō)明

Daikin PTFE (polytetrafluoroethylene) molding powders are excellent, fine cut resins, well suited for a variety of demanding chemical, mechanical, electrical and non-stick surface applications. These PTFE resins are fully fluorinated and have the best thermal, electrical, and chemical properties of all fluoropolymers with a continuous service rating of 500°F (260°C). Daikin PTFE molding powders are available in homopolymer and modified fine cut grades.

Daikin PTFE molding powders can be used continuously at temperatures up to 260°C (500°F) and for short periods of time at higher temperatures. They also possess excellent low temperature strength.

Daikin PTFE molding powders are completely inert to attack by all chemicals except hightemperature, high-pressure elemental fluorine gas, molten alkaline metals and chlorine trifluoride.

The non-polar molecular structure makes Daikin PTFE molding powders ideal for use as high-frequency insulating material. The dielectric constant and dissipation factor are uniformly low over a wide frequency range.

Under ordinary conditions of use, Daikin PTFE molding powders possess the lowest coefficient of friction of any solid material. Also, the non-stick properties of these products prevent most materials from adhering to them.

Chemical/Mechanical—Packings, gaskets, diaphragms, bellows, corrosion-resistant linings, piping components, pump parts, O-rings, V-rings, bushings, slide bearings, etc.

Electrical/Other—Insulating skived tape, insulating sleeves, terminals, connectors, sockets, spacers, electronic parts, laboratory equipment, etc.

總體

材料狀態(tài) • 已商用：當(dāng)前有效   
供貨地區(qū) • 北美洲   
填料/增強(qiáng)材料 • 未指定填料\增強(qiáng)材料   
 • 低摩擦系數(shù) • 均聚物 • 粘度，高 
性能特點(diǎn) • 低溫強(qiáng)度 • 耐化學(xué)性良好  
 • 高分子量 • 無(wú)粘性  
 • 包裝 • 墊圈 • 實(shí)驗(yàn)室器具 
 • 泵件 • 隔膜  
   • 套管 
用途 • 襯里 • 管道系統(tǒng)  
   • 一般目的 
 • 帶子 • 絕緣屏蔽  
   • 軸承 
 • 電氣部件 • 連接器  
    
機(jī)構(gòu)評(píng)級(jí) • FDA 21 CFR 177.1550   
形式 • 粉狀   
加工方法 • 燒結(jié) • 壓縮模塑  

物理性能  額定值單位制 測(cè)試方法
比重  2.16g/cm³ ASTM D4894
表觀密度  0.48g/cm³ ASTM D4894
收縮率 - 流動(dòng) 3.2% Internal Method
機(jī)械性能  額定值單位制 測(cè)試方法
抗張強(qiáng)度 (屈服, 1.50 mm) 43.0MPa ASTM D4894
伸長(zhǎng)率 (斷裂, 1.50 mm) 400% ASTM D4894
壓縮強(qiáng)度   ASTM D695
0% 應(yīng)變 2 7.80MPa 
1% 應(yīng)變 3 5.00MPa 
25% 應(yīng)變 3 28.1MPa 
負(fù)載變形   ASTM D621
25°C, 14 MPa 17.2% 
100°C, 14 MPa 33.3% 
200°C, 6.9 MPa 27.0% 
彈性體  額定值單位制 測(cè)試方法
壓縮永久變形  ASTM D621
25°C 4  8.6% 
100°C 4  20% 
200°C 5  16% 
1 / 2   
  
  
   
  
  
 
POLYFLON™ M-18  2012年9月29日
聚四氟乙烯  
DAIKIN AMERICA, INC.  
熱性能 額定值單位制 測(cè)試方法
最高連續(xù)使用溫度 260°C 
熔融溫度 327°C DSC
電氣性能 額定值單位制 測(cè)試方法
表面電阻率 > 1.0E+15ohm ASTM D257
體積電阻率 > 1.0E+18ohm•cm ASTM D257
介電強(qiáng)度 100kV/mm 
介電常數(shù) (1 kHz) < 2.10 ASTM D150
耗散因數(shù) (1 kHz) < 0.00010 ASTM D150
補(bǔ)充信息 額定值單位制 測(cè)試方法
MIT Flexural Life 5.00E+6 ASTM D2178
Stretching Void Index 300 ASTM D4895

備注
1 一般屬性：這些不能被視為規(guī)格。

2 off set, 10x20 mm sample

3 10x20 mm sample

4 13.7 MPa

5 6.9 MPa