Sichuan Deyang Chemical Co., Ltd

產品說明

PPS/PTFE-hGR203 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows solvent resistance, abrasive resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage, good dimensional stability.

Owing to its high performance, it's widely used in mechanical and chemical industry for making wearable parts/components which work in the high-temperature, high pressure and solvent circumstance. Such as: plastic axle bearing, axle sleeve, textile machine components, components which are used in aero industry.

總體

材料狀態 • 已商用：當前有效  
供貨地區 • 亞太地區  
填料/增強材料 • 玻璃纖維增強材料  
添加劑 • PTFE潤滑劑  
 • 尺寸穩定性良好 • 可加工性，良好 • 耐熱性，高
性能特點 • 經潤滑 • 耐磨蝕性，良好 • 收縮性低
 • 抗溶解性 • 耐磨損性良好 • 阻燃性能
用途 • 工業領域： • 航空航天應用 • 醫療/護理領域的應用
加工方法 • 注射成型  

物理性能 額定值單位制 測試方法
密度 1.52g/cm³ Internal Method
收縮率 - 流動 0.25% Internal Method
機械性能 額定值單位制 測試方法
抗張強度 126MPa Internal Method
伸長率 (斷裂) 1.8% Internal Method
彎曲模量 8500MPa Internal Method
彎曲強度 174MPa Internal Method
摩擦系數 0.37 Internal Method
Abrasion - Width 6mm Internal Method
磨損量 2 4.5mg Internal Method
沖擊性能 額定值單位制 測試方法
懸壁梁缺口沖擊強度 11kJ/m² Internal Method
硬度 額定值單位制 測試方法
洛氏硬度 3 104 Internal Method
熱性能 額定值單位制 測試方法
熱變形溫度 (1.8 MPa, 未退火) 266°C Internal Method
熔融溫度 281°C Internal Method
可燃性 額定值單位制 測試方法
UL 阻燃等級 V-0 Internal Method
  
注射 額定值單位制 
干燥溫度 110 到 140°C 
干燥時間 3.0 到 5.0hr 
螺筒后部溫度 270 到 290°C 
螺筒中部溫度 300 到 320°C 
螺筒前部溫度 300 到 320°C 
射嘴溫度 290 到 320°C 
加工（熔體）溫度 160°C 
模具溫度 100 到 150°C 
注塑溫度 50.0 到 100MPa 
背壓 0.100 到 1.00MPa 
螺桿轉速 40 到 100rpm 
注射說明  
Processing time: 2 to 8hr  
1 / 2  
  
  
  
  
  
 
China PPS PTFE-hGR203 2012年9月29日
聚苯硫醚
Sichuan Deyang Chemical Co., Ltd
備注
1 一般屬性：這些不能被視為規格。

2 120 min

3 HR

2 / 2