Teflon® FEP 106-N
聚全氟乙烯-丙烯樹脂
DuPont Fluoropolymers

產品說明

Teflon® 106-N is one of DuPonts melt processable copolymers of tetrafluoroethylene and hexafluoropropylene.

It offers the excellent combination of properties characteristic of Teflon® fluoropolymer resins: non-ageing characteristics, chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption and excellent weather resistance.

Teflon® 106-N has the lowest molecular weight of all Teflon® FEP grades. It is designed for the production, by the extrusion process, of thin wall, small diameter wire insulations, and small diameter tubes. It can also be used for the production of intricate and thin wall parts made by the injection moulding process.

Teflon® 106-N is a "high productivity" grade of Teflon® FEP. At processing temperatures it shows low viscosity and a high critical shear rate. Compared to the general purpose grade Teflon® 100-N, it can be extruded, in similar wire constructions, at much faster rates and higher extrusion line speeds, and the final product will show comparable physical properties.

總體

材料狀態 • 已商用：當前有效   
供貨地區 • 北美洲 • 歐洲  
 • 南美洲 • 亞太地區  
    
 • 低分子量 • 良好的柔韌性 • 耐熱性，高 
性能特點 • 低摩擦系數 • 耐化學性良好 • 韌性良好 
 • 低粘度 • 耐氣候影響性能良好 • 吸潮性差 
用途 • 薄壁包裝 • 電線電纜應用  
形式 • 顆粒料   
加工方法 • 擠出 • 注射成型  

物理性能 額定值單位制 測試方法 
比重   
-- 2.11 到 2.16g/cm³ ASTM D792 
-- 2.12 到 2.17g/cm³ ISO 1183 
表觀密度 1.30g/cm³ Internal Method 
  ISO 60 
   
熔流率 (372°C/5.0 kg) 22g/10 min ASTM D2116 
  ISO 12086 
   
 

吸水率 (24 hr)

機械性能

抗張強度 (屈服, 23°C)

伸長率 (斷裂, 23°C)

彎曲模量 (23°C)

硬度

硬度計硬度 (邵氏 D)

熱性能
最高連續使用溫度 2
 

< 0.010% ASTM D570 
額定值單位制 測試方法 
20.0MPa ASTM D638 
 ISO 12086 
  
300% ASTM D638 
 ISO 12086 
  
655MPa ASTM D790 
 ISO 178 
  
額定值單位制 測試方法 

55 ASTM D2240 ISO 868

額定值單位制 測試方法

205°C
 

熔融溫度 3 255°C 
線形膨脹系數 - 流動 (38 到 71°C) 0.000094cm/cm/°C ASTM D696
比熱 1090J/kg/°C ASTM C351
導熱系數 0.24W/m/K ASTM C177
電氣性能 額定值單位制 測試方法
體積電阻率  
-- > 1.0E+18ohm•cm ASTM D257
-- 1.0E+18ohm•cm IEC 60093

1 / 2

 
 
 
 
 
 
Teflon® FEP 106-N  2012年9月30日 
聚全氟乙烯-丙烯樹脂   
DuPont Fluoropolymers   
電氣性能  額定值單位制 測試方法 
介電強度    
0.250 mm 4 80kV/mm ASTM D149 
3.20 mm 4 20kV/mm ASTM D149 
0.250 mm 80kV/mm IEC 60243-1 
3.20 mm 20kV/mm IEC 60243-1 
介電常數 5 (500 MHz) 2.10 ASTM D150 
   IEC 60250 
耗散因數 5 (500 MHz) 0.00051 ASTM D150 
   IEC 60250 
可燃性  額定值單位制 測試方法 
燃燒速率  < 60mm/min ASTM D635 
極限氧指數 > 95% ASTM D2863 
  ISO 4589-2 
    
補充信息  額定值單位制 測試方法 
MIT Folding Endurance - film (180.0 到 200.0 µm) 5.0E+3Cycles ASTM D2176 
CLTE, FLow, ASTM D696, 38 to 71°C: 83e-6 to 104e-6 cm/cm/°C   
Dissipation factor, ASTM D150, 60 to 1e9 Hz: 0.0002 to 0.001   
Relative permittivity, IEC 250, 60 to 1e9 Hz: 2.1   
Dissipation Factor, IEC 250, 60 to 1e9 Hz: 0.0002 to 0.001   
Rate of burning, ASTM D635, 5 mm: < 5 s   

備注
1 一般屬性：這些不能被視為規格。

2 ASTM D4519/ D3418

3 ASTM D4591 / D3418

4 方法A（短時間）

5 60 to 1e9 Hz